Metal Alloys Corporation
Engineers India Limited Engineers India Limited Metal Alloys Corporation {short description of image}

 ISO
Home About us Products Our Special Product Manufacturing Process Alloys Range Industrial Application Media Gallery Contact us
Metal Alloys CorporationMetal Alloys CorporationMetal Alloys CorporationMetal Alloys CorporationMetal Alloys CorporationMetal Alloys CorporationMetal Alloys Corporation

Metal Alloys Corporation

Product Range

 

Metal Alloys Corporation

Home » Silicon Aluminium Bronze Hollow Rods
CATEGORY
 ASTM BS EN JIS DIN ISO IS
Silicon Aluminum Bronze C63600 CuAl3Si

Silicon Aluminium Bronze Hollow Rods

C63600 Silicon Aluminium Bronze Hollow Rods

C63600 Silicon Aluminium Bronze Hollow Rods
Ask for Price
PDF
The C63600 Silicon Aluminum Bronze possess good hot and cold workability, forging ability. The alloy is fabricated by bending, coining, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.

Typical Applications:
  • Electrical : Cold Headed Nuts, Cable Connectors, Components for Pole Line Hardware
  • Fasteners : Screw Machine Products, Bolts
  • Industrial : Valve Components, Nuclear Power Service

Chemical Composition
Al As Cu Fe Pb Ni Si Sn Zn
Min/Max 3.0 - 4.0 0.15 Rem 0.15 0.05 0.15 0.7 - 1.3 0.2 0.5
Nominals 3.5 - 95.5 - - - 1 - -

Physical Properties
Product Property US Customary Metric
Coefficient of Thermal Expansion 9.4 10−6Per °F (68-572 F) 16.9 10−6Per °F (20-300 C)
Density 0.301 lb/in3 at 68 F 8.33 gm/cm3 @ 20 C
Electrical Conductivity 12 %IACS @ 68 F 0.07 MegaSiemens/cm @ 20 C
Electrical Resistivity 86.4 ohms-cmil/ft @ 68 F 14.36 microhm-cm @ 20 C
Melting Point - Liquidus 1890 F 1032 C
Modulas of Elasticity in Tension 16000 ksi 110000 MPa
Specific Gravity 8.33 8.33
Thermal Conductivity 33.0 BTU in/hr.ft2.°F ) at 68F 57.1 W/m · oK at 20 C

Fabrication:
Joining Technique Suitability
Brazing Not Recommended
Butt Weld Fair
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Fair
Coated Metal Arc Welding Fair
Gas Shielded Arc Welding Fair
Machinability Rating 40
Oxyacetylene Welding Not Recommended
Seam Weld Fair
Soldering Not Recommended
Spot Weld Fair

Sizes Available
ROUND RODS 8mm To 70 mm
HEX 10mm To 60mm
SQUARE 10mm To 60mm
FLAT 10mm Min Thickness and max Width 120mm
BILLETS Up to 200 mm
INGOTS As per Specification


Yes! I am Interested


CATEGORY
 ASTM BS EN JIS DIN ISO IS
Silicon Aluminum Bronze C64200 CA107 CW301G CuAl7Si2 CuAl7Si2 IS 10569 CuAl7Si2

C64200 Silicon Aluminium Bronze Hollow Rods

C64200 Silicon Aluminium Bronze Hollow Rods
Ask for Price
PDF
ASTM B249, QQ-C-465, AMS 4631, AMS 4634, EU
Designation: CuAl7Si2, CW302G The C64200 silicone aluminum alloy is an engineering alloy which is resistant to corrosion as copper and is much stronger. Is is manufactured in round, hexagonal and octagonal rods for hot forming and free machining. It is considered as best valve stem alloy and its other applications include gears, marine hardware, nuts, pole line hardware, and valve bodies and components.
Typical Applications:
  • Automotive : Valve Guides, Automobile Engine
  • Electrical: Pole Line Hardware
  • Fasteners: Bolts, Nuts
  • Industrial: Valve Components, Valve Bodies, Gears, Valve Stems, Cams
  • Industrial: Marine: Hardware

Equivalent Specifications
SPECIFICATIONSDESIGNATION
ISOCuAl7Si2
EuropenCuAl7Si2
UNSC64210

Chemical Composition
AlAsCuFePbMnNiSiSnZn
Min/Max6.3 - 7.60.15Rem0.30.050.10.251.5 - 2.20.20.5
Nominals7-91.2- ---1.8--

Physical Properties
End Product Specification
Bar AMS 4631, ASME SB150, ASTM B150
Bar, Forging ASTM B124
Bolts ASTM F468
Forgings, Die AMS 4631, ASME SB283, ASTM B283
Nuts ASTM F467
Rod AMS 4631, ASME SB150, ASTM B150, SAE J463, J461
Rod, Forging ASTM B124
Screws ASTM F468
Shapes ASTM B150
Shapes, Forging ASTM B124
Studs ASTM F468

Fabrication :
Joining Technique Suitability
Brazing Fair
Butt Weld Fair
Capacity for Being Cold Worked Poor
Capacity for Being Hot Formed Excellent
Coated Metal Arc Welding Fair
Gas Shielded Arc Welding Fair
Machinability Rating 80
Oxyacetylene Welding Not Recommended
Seam Weld Fair
Soldering Not Recommended
Spot Weld Fair

Physical Properties :
Product Property US Customary ">Metric
Coefficient of Thermal Expansion 10.0 10−6Per °F (68-572 F) 18.0 10−6Per °F (20-300 C)
Density 0.278 lb/in3 at 68 F 7.7 gm/cm3 @ 20 C
Electrical Conductivity 8 %IACS @ 68 F 0.047 MegaSiemens/cm @ 20 C
Electrical Resistivity 113.0 ohms-cmil/ft @ 68 F 18.79 microhm-cm @ 20 C
Melting Point - Liquidus 1840 F 1004 C
Melting Point - Solidus 1800 F 982 C
Modulas of Elasticity in Tension 16000 ksi 110000 MPa
Modulus of Rigidity 6000 ksi 41370 MPa
Specific Gravity 7.69 7.69
Specific Heat Capacity 0.09 Btu/lb/·oF at 68F 377.1 J/kg ·oK at 293 K
Thermal Conductivity 26.0 BTU in/hr.ft2.°F ) at 68F 45.0 W/m · oK at 20 C

Sizes Available:
ROUND RODS 8mm To 70 mm
HEX 10mm To 60mm
SQUARE 10mm To 60mm
FLAT 10mm Min Thickness and max Width 120mm
BILLETS Up to 200 mm
INGOTS As per Specification


Yes! I am Interested


CATEGORY
 ASTM BS EN JIS DIN ISO IS
Low Silicon Bronze "B" C65100 CW115C 2.049 1187-CuSi1

C65100 Low Silicon Bronze Hollow Rods

C65100 Low Silicon Bronze Hollow Rods
Ask for Price
PDF
C65100 Low Silicon Bronze "B" is an engineering alloy resistant to corrosion as copper itself, but much stronger, and with good fatigue endurance. The alloy is appreciated for its brazing ability, strength, corrosion resistance and electrical properties and serves as one of the most weldable copper alloys. The alloy can be joined by using resistance welding, soldering or brazing. The alloy is joined by gas shield arc welding, spot welding and also by oxyacetylene welding.

Typical Applications:
  • Electrical: Conduit, Pole Line Hardware,Motor, Rotor Bars
  • Fasteners: Bolts, Cable Clamps, Cap Screws, Machine Screws, Nuts, Rivets, U Bolts, Fasteners, Screws
  • Industrial: Oil Refinery Plumbing Tube, Heat Exchanger Tube, Welding Rod, Hydraulic Pressure Lines
  • Marine: Hardware

Equivalent Specifications
SPECIFICATIONSDESIGNATION
ISOCuSi1
EuropenCuSi1

Chemical Composition
CuFePbMnSiZn
Min/MaxRem0.80.050.70.80 - 2.01.5
Nominals98.5 ---1.5-

End Product Specification
Bar ASME SB98, ASTM B98
Bolts ASTM F468
Nuts ASTM F467
Pipe ASTM B315
Plate ASTM B96
Plate, Clad ASTM B432
Rod ASME SB98, ASTM B98
Screws ASTM F468
Shapes ASME SB98, ASTM B98
Sheet ASTM B96
Strip ASTM B96
Studs ASTM F468
Tube ASTM B315
Wire ASTM B99, B105

Fabrication:
Joining Technique Suitability
Brazing Excellent
Butt Weld Excellent
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Excellent
Coated Metal Arc Welding Fair
Gas Shielded Arc Welding Excellent
Machinability Rating 30
Oxyacetylene Welding Good
Seam Weld Good
Soldering Excellent
Spot Weld Excellent

Physical Properties:
Product Property US Customary Metric
Coefficient of Thermal Expansion 9.9 10−6Per °F (68-212 F) 17.8 10−6Per °F (20-100 C)
Density 0.316 lb/in3 at 68 F 8.75 gm/cm3 @ 20 C
Electrical Conductivity 12 %IACS @ 68 F 0.07 MegaSiemens/cm @ 20 C
Electrical Resistivity 86.4 ohms-cmil/ft @ 68 F 14.36 microhm-cm @ 20 C
Melting Point - Liquidus 1940 F 1060 C
Melting Point - Solidus 1890 F 1032 C
Modulas of Elasticity in Tension 17000 ksi 117000 MPa
Modulus of Rigidity 6400 ksi 44130 MPa
Specific Gravity 8.75 8.75
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · oK at 293 K
Thermal Conductivity 33.0 BTU in/hr.ft2.°F ) at 68F 57.1 W/m · oK at 20 C

Sizes Available
ROUND RODS/BARS 8mm To 70 mm
HEX 10mm To 60mm
SQUARE 10mm To 60mm
FLAT 10mm Min Thickness and max Width 120mm
BILLETS Up to 200 mm
INGOTS As per Specification


Yes! I am Interested


CATEGORY
 ASTM BS EN JIS DIN ISO IS
High Silicon Bronze "A" C65500 CS101 CW116C 2.1525 R1187-CuSi3Mn1

C65500 High Silicon Bronze Hollow Rods

C65500 High Silicon Bronze Hollow Rods
Ask for Price
PDF
ASTM B96, ASTM B248, ASTM B98 The silicon bronze C65500 is a high strength, engineering alloy with having resistance against corrosion from fresh and salt water, acids, alkalies, salts and organic chemicals. The alloy is not suitable to be used with sulfides, nitric acid, acid chromates or oxidizing salts such as ferric chloride. The alloy possess strength, resilience and formability and is non-sparking, galling resistant and fatigue resistant.

The applications of C65500 include electrical conduit, pump shafts, valve stems, tie rods, fasteners, marine and pole-line hardware, nuts, bolts, screws, rivets, nails, bushings, screen cloth and wire.

Typical Applications:
  • Electrical: Sculptures,Electrical,Pole Line Hardware,Motors,Rotor Bar
  • Fasteners: Screws,Rivets,Burrs,Nuts,Nails,Cotter Pins,Clamps,Bolts,Hinges
  • Industrial: Screen Cloth,Wear Plates,Screen Plates,Shafting,Wire,Welded Pressure Vessels,Oil Refinery Plumbing Tube,Bearing Plates,Butts
  • Marine:  Vessel Hardware ,Propeller Shaft

Equivalent Specifications
SPECIFICATIONSDESIGNATION
ISOCuSi3Mn1
EuropenCuSi3Mn1
BSCS 101
RussianBrKMo3-1

Chemical Composition Chemical Composition:
  Cu Fe Pb Mn Ni Si Zn
Min/Max Rem 0.8 0.05 0.50 - 1.3 0.6 2.8 - 3.8 1.5
Nominals 97.0000 - - 0.9000 3.0000 -

Specifications:
End Product Specification
Bar SAE J463, J461
Bar, Forging ASTM B124
Bar, Rolled, Pressure Vessels ASME SB96, ASTM B96
Bolts ASTM F468
Forgings, Die ASTM B283
Nuts ASTM F467
Pipe ASME SB315, ASTM B315
Plate ASME SB96, ASTM B96
Plate, Bridge and Bearing ASTM B100
Plate, Clad ASTM B432
Plate, Pressure Vessels ASME SB96, ASTM B96
Rod ASME SB98, ASTM B98, SAE J461, J463
Rod, Forging ASTM B124
Screws ASTM F468
Shapes ASME SB98, ASTM B98, SAE J461, J463
Shapes, Forging ASTM B124
Sheet ASME SB96, ASTM B96, SAE J461, J463
Sheet, Bridge and Bearing ASTM B100
Sheet, Pressure Vessels ASME SB96, ASTM B96
Strip ASME SB96, ASTM B96, SAE J461, J463
Studs ASTM F468
Tube ASME SB315, ASTM B315, MILITARY MIL-T-8231
Wire ASTM B105, B99

Fabrication:
Joining Technique Suitability
Brazing Excellent
Butt Weld Excellent
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Excellent
Coated Metal Arc Welding Fair
Forgeability Rating 40
Gas Shielded Arc Welding Excellent
Machinability Rating 30
Oxyacetylene Welding Good
Seam Weld Excellent
Soldering Good
Spot Weld Excellent

Physical Properties:
Product Property US Customary Metric
Coefficient of Thermal Expansion 10.0 10−6Per °F (68-212 F) 18.0 ·10-6 per oC (20-100 C)
Density 0.308 lb/in3 at 68 F 8.53 gm/cm3 @ 20 C
Electrical Conductivity 7 %IACS @ 68 F 0.041 MegaSiemens/cm @ 20 C
Electrical Resistivity 148.0 ohms-cmil/ft @ 68 F 24.6 microhm-cm @ 20 C
Melting Point - Liquidus 1880 F 1027 C
Melting Point - Solidus 1780 F 971 C
Modulas of Elasticity in Tension 15000 ksi 103400 MPa
Modulus of Rigidity 5600 ksi 38610 MPa
Specific Gravity 8.53 8.53
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · oK at 293 K
Thermal Conductivity 21.0.0 BTU in/hr.ft2.°F ) at 68F 36.3 W/m · oK at 20 C

Sizes Available
ROUND RODS 8mm To 70 mm
HEX 10mm To 60mm
SQUARE 10mm To 60mm
FLAT 10mm Min Thickness and max Width 120mm
BILLETS Up to 200 mm
INGOTS As per Specification


Yes! I am Interested


CATEGORY
 ASTM BS EN JIS DIN ISO IS
Silicon Bronze (AMS 4616) C65620 CW009A CuSi3Fe2Sn3

C65620 Silicon Bronze Hollow Rods

C65620 Silicon Bronze Hollow Rods
Ask for Price
PDF
C65620 Silicon Bronze Rods (AMS 4616) is an engineering alloy resistant to corrosion as copper itself, but much stronger, and with good fatigue endurance. The alloy is appreciated for its brazing ability, strength, corrosion resistance and electrical properties and serves as one of the most weldable copper alloys. The alloy can be joined by using resistance welding, soldering or brazing. The alloy is joined by gas shield arc welding, spot welding and also by oxyacetylene welding.

Typical Applications:
  • Electrical: Sculptures,Electrical,Pole Line Hardware,Motors,Rotor Bar
  • Fasteners: Screws,Rivets,Burrs,Nuts,Nails,Cotter Pins,Clamps,Bolts,Hinges
  • Industrial: Screen Cloth,Wear Plates,Screen Plates,Shafting,Wire,Welded Pressure Vessels,Oil Refinery Plumbing Tube,Bearing Plates,Butts
  • Marine:  Vessel Hardware ,Propeller Shaft

Equivalent Specifications
SPECIFICATIONSDESIGNATION
ISOCuSi1
EuropenCuSi1

Chemical Composition Chemical Composition:
  Cu Fe Pb Mn Ni Si
Min/Max Rem 0.8 0.05 0.7 0.80 - 2.0 1.5
Nominals 98.5 - - - 1.5 -

Specifications:
End Product Specification
Bar ASME SB98, ASTM B98
Bolts ASTM F468
Nuts ASTM F467
Pipe ASTM B315
Plate ASTM B96
Plate, Clad ASTM B432
Rod ASME SB98, ASTM B98
Screws ASTM F468
Shapes ASME SB98, ASTM B98
Sheet ASTM B96
Strip ASTM B96
Studs ASTM F468
Tube ASTM B315
Wire ASTM B99, B105

Fabrication:
Joining Technique Suitability
Brazing Excellent
Butt Weld Excellent
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Excellent
Coated Metal Arc Welding Fair
Gas Shielded Arc Welding Excellent
Machinability Rating 30
Oxyacetylene Welding Good
Seam Weld Excellent
Soldering Good
Spot Weld Excellent

Physical Properties:
Product Property US Customary Metric
Coefficient of Thermal Expansion 9.9 10−6Per °F (68-212 F) 17.8 10−6Per °F (20-100 C)
Density 0.316 lb/in3 at 68 F 8.75 gm/cm3 @ 20 C
Electrical Conductivity 12 %IACS @ 68 F 0.07 MegaSiemens/cm @ 20 C
Electrical Resistivity 86.4 ohms-cmil/ft @ 68 F 14.36 microhm-cm @ 20 C
Melting Point - Liquidus 1940 F 1060 C
Melting Point - Solidus 1890 F 1032 C
Modulas of Elasticity in Tension 17000 ksi 117000 MPa
Modulus of Rigidity 6400 ksi 44130 MPa
Specific Gravity 8.75 8.75
Specific Heat Capacity 0.09 Btu/lb/°F at 68 F 377.1 J/kg · oK at 293 K
Thermal Conductivity 33.0 BTU in/hr.ft2.°F 57.1 W/m · oK at 20 C

Sizes Available
ROUND RODS 8mm To 70 mm
HEX 10mm To 60mm
SQUARE 10mm To 60mm
FLAT 10mm Min Thickness and max Width 120mm
BILLETS Up to 200 mm
INGOTS As per Specification


Yes! I am Interested


Home  |  About us  |  Products  |  Our Special Product  |  Manufacturing Process  |  Alloys Range  |  Industrial Application  |  Media Gallery  |  Contact Us  |  Send Enquiry

Member INDIAMART© Metal Alloys Corporation. All Rights Reserved (Terms of Use)
Developed and Managed by IndiaMART InterMESH Limited