Low Lead Brass Tubes

C27450 Lead Free Brass to not only aid in lead free compliance, but to optimize manufacturing efficiencies through productivity & complete recyclability.

Typical Applications:

Potable water components, fixtures & applications
PEX plumbing applications & systems
Forged products requiring lead free &/or dezincification compliance

Advantages:

Good machineability
Excellent ability to Thread Roll
Dezincification Resistant
Excellent forgeability
Excellent Brazing & Plating

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	CuZn37
Europen	CW508L
BS	-
JIS	C27450
Russian	-

Chemical Composition

	Cu	Pb	Fe	Zn	Others
Min/Max	60-65	<0.25 (max)	0.35	Rem	<0.5
Nominals	63.00	-	-	37.00	-

Fabrication Properties

Soldering	Excellent
Brazing	Excellent
Cold working	Excellent
Plating	Excellent
Forgability	95
Machinability	70

Sizes Available

WIRE	1mm To 8mm
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

C33000 brass tubing, a yellow brass that is both formable and machinable. C330 is only produced in tube form and is generally suitable for minimal corrosive conditions. The lead content prevents from successful welding, but common machine processes include: machining, forming, piercing, and punching.

Typical Applications:

Pump Cylinder Liners
Pump Lines
Plumbing Accessories
Power Cylinders Primers
J Bends

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	C330
Europen	CW705R
BS	-
JIS	C33000
Russian	-

Chemical Composition

	Cu	Pb	Fe	Sn	Zn
Min/Max	58-61	0.25-0.70	0.15 (max)	0.25 (max)	Rem
Nominals	60.00	-	-	0.7000	40.00

Mechanical Properties

	Cu	Pb	Fe	Zn
Min/Max	65.0-68.0	0.25-0.7	0.07	Rem
Nominals	66.00	0.50	-	33.5

Fabrication Properties:

Joining Technique Suitability	Suitability
Soldering	Excellent
Brazing	Good
Oxyacethlene Welding	Fair
Gas Shielded Arc Welding	Fair
Coated Metal Arc Welding	Not Recommended
Spot Weld	Fair
Seam Weld	Not Recommended
Butt Weld	Fair
Capacity for Being Cold Worked	Excellent
Capacity for Being Hot Formed	Poor
Machinability Rating	60

Sizes Available

WIRE	1mm To 8mm
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

C36300 alloy provides a lower lead brass alloy option that aids with the compliance strategies of manufacturers who seek an alternative that is not only COMPLIANT, but also COMPETITIVE and COMPATIBLE with standard free cutting and forgings alloys commonly used today.

Typical Applications:

Screw machine parts and components for potable water products requiring lead free compliance
Forged parts and components for potable water products requiring lead free compliance

Advantages:

Excellent machineabilitys
Excellent capability for brazing and plating
Improved resistance to dezincification
Good hot Forgability
Excellent ability to thread roll

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	CuZn37
Europen	CW508L
BS	-
JIS	C36300
Russian	-

Chemical Composition

	Cu	Pb	Fe	P	Zn
Min/Max	61-63	0.25-0.70	0.15 (max)	0.04-0.15	Rem
Nominals	63.00	-	-	-	37.00

Mechanical Composition

Rod H02	Tensile Strength (ksi)	Yield Strength (ksi)	Elongation (%)	Hardness (Rb)
	65	45	20%	75

Sizes Available

WIRE	1mm To 8mm
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

C36500 alloy provides a lower percentage lead alloy (versus conventional free cutting and forging alloys) that aids in the compliance to this legislation while maintaining machinability ratings near that of conventional free cutting brass.

Typical Applications:

Screw machine parts requiring lower lead content
Potable water components, fixtures & applications
Forged components in lead free compliant products

Advantages:

Excellent machineabilitys
Excellent capability for brazing and plating
Completely recyclable
Good hot Forgability
Excellent ability to thread roll

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	CuZn40Pb
Europen	CW610N
BS	-
JIS	C36500
Russian	-

Chemical Composition

	Cu	Pb	Fe	P	Zn
Min/Max	58-61	0.25-0.70	0.15 (max)	0.25 (max)	Rem
Nominals	60.00	-	-	-	37.00

Mechanical Composition

Rod H02	Tensile Strength (ksi)	Yield Strength (ksi)	Elongation (%)	Hardness (Rb)
	65	45	30%	75

Sizes Available

WIRE	1mm To 8mm
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.

Typical Applications:

Typical Uses: Industrial, Automotive Screw Machine Parts

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
Europen	CuZn38Pb1
BS	CZ-129
JIS	CuZn39Pb1
Russian	LS63-3

Chemical Composition

	Cu	Fe	Pb	Zn
Min/Max	59.0 - 62.0	0-0.15	0.8-1.5	Rem
Nominals	61.5000	-	1.0	-

Physical Properties

Melting Point - LiquidusÂ°F	1650
Melting Point - SolidusÂ°F	1630
Densitylb/cu in. at 68Â°F	0.304F
Specific Gravity	8.41
Electrical Conductivity% IACS at 68Â°F	27
Thermal ConductivityBtu/ sq ft/ ft hr/ Â°F at 68Â°F	69
Coefficient of Thermal Expansion 68-572 10⁻⁶Per °F (68-572 F)	11.6
Specific Heat CapacityBtu/lb/°F at 68°F	0.09
Modulus of Elasticity in Tensionksi	15000
Modulus of Rigidityksi	5600

Sizes Available

HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

C33000 brass tubing, a yellow brass that is both formable and machinable. C330 is only produced in tube form and is generally suitable for minimal corrosive conditions. The lead content prevents from successful welding, but common machine processes include: machining, forming, piercing, and punching.

Typical Applications:

Pump Cylinder Liners
Pump Lines
Plumbing Accessories
Power Cylinders Primers
J Bends

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	C330
Europen	CW705R
BS	-
JIS	C33000
Russian	-

Chemical Composition

	Cu	Pb	Fe	Sn	Zn
Min/Max	58-61	0.25-0.70	0.15 (max)	0.25 (max)	Rem
Nominals	60.00	-	-		40.00

Mechanical Properties

	Cu	Pb	Fe	Zn
Min/Max	65.0-68.0	0.25-0.7	0.07	Rem
Nominals	66.00	0.50	-	33.5

Fabrication Properties:

Joining Technique	Suitability
Soldering	Excellent
Brazing	Good
Oxyacethlene Welding	Fair
Gas Shielded Arc Welding	Fair
Coated Metal Arc Welding	Not Recommended
Spot Weld	Fair
Seam Weld	Not Recommended
Butt Weld	Fair
Capacity for Being Cold Worked	Excellent
Capacity for Being Hot Formed	Poor
Machinability Rating	60

Sizes Available

WIRE	1mm To 8mm
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

C33000 brass tubing, a yellow brass that is both formable and machinable. C330 is only produced in tube form and is generally suitable for minimal corrosive conditions. The lead content prevents from successful welding, but common machine processes include: machining, forming, piercing, and punching.

Typical Applications:

Pump Cylinder Liners
Pump Lines
Plumbing Accessories
Power Cylinders Primers
J Bends

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	C330
Europen	CW705R
BS	-
JIS	C33000
Russian	-

Chemical Composition

	Cu	Pb	Fe	Sn	Zn
Min/Max	58-61	0.25-0.70	0.15 (max)	0.25 (max)	Rem
Nominals	60.0000	-	-	-	40.00

Mechanical Properties

	Cu	Pb	Fe	Zn
Min/Max	65.0-68.0	0.25-0.7	0.07	Rem
Nominals	66.00	0.50	-	33.5

Fabrication Properties:

Joining Technique	Suitability
Soldering	Excellent
Brazing	Good
Oxyacethlene Welding	Fair
Gas Shielded Arc Welding	Fair
Coated Metal Arc Welding	Not Recommended
Spot Weld	Fair
Seam Weld	Not Recommended
Butt Weld	Fair
Capacity for Being Cold Worked	Excellent
Capacity for Being Hot Formed	Poor
Machinability Rating	60

Sizes Available

WIRE	1mm To 8mm
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

Ask for Price

Muntz Metal (C28000 or C280) was founded and patented in 1832 by English businessman George F. Muntz. One of the most diserable features of Muntz metal is it's distinctive color. This particular metal is primarily used in architectural applications. Muntz metal is a highly plastic metal at red heat, making it an ideal choice for pressing, stamping and hot forging. Other advantages that C280 lends are: high ductility, high electrical and thermal conductivity, high impact strength, good creep resistance, ease of welding, and low volatility under high vacuum.

Typical Applications:

Architectural applications
Decorative Hardware
Condenser plates
Heat Exchanger Tube
Valve Stems
Brazing Rod

Equivalent Specifications

SPECIFICATIONS	DESIGNATION
ISO	CuZn40
Europen	CuZn40
BS	CZ 109
JIS	C 2800
Russian	L60

Chemical Composition

	Cu	Fe	Pb	Zn
Min/Max	59.0 - 63.0	0.07	0.3	Rem
Nominals	60.0000	-	-	40.0000

Physical Properties

Coefficient of Thermal Expansion	11.60 10⁻⁶Per °F (68-572 F)
Density	0.303 lb/in3 @ 68 F
Electrical Conductivity	28 %IACS @ 68 F
Electrical Resistivity	37.0 ohms-cmil/ft @ 68 F
Melting Point Liquid US	1660 F
Melting Point Solid US	1650 F
Modulas of Elasticity in Tension	15000 ksi
Modulas of Rigidity	5600 ksi
Specific Gravity	8.39
Specific Heat Capacity	0.09 Btu/lb/°F @ 68 F
Thermal Conductivity	71.0 BTU in/hr.ft².°F @ 68 F

Sizes Available

HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS/RODS	6mm To 130 mm
HEX	5mm To 60mm
SQUARE	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
PROFILES / SECTIONS	AS per Customer Drawing
BILLETS	Up to 200 mm
INGOTS	AS per Specification

CATEGORY	ASTM	BS	EN	JIS	DIN	ISO	IS
Yellow Brass	C27450	CZ109	CW509L		2.036	Cuzn37

C27450 Low Lead Brass Tubes

C33000 Low Lead Brass Tubes

C36300 Low Lead Brass Tubes

C36500 Low Lead Brass Tubes

C37000 Muntz Metal Brass Pipes

CW705R Low Lead Brass Pipes

C330 Low Lead Brass Pipes

Cuzn40 Low Lead Brass Pipes